Green Synthesized BSA-Coated Selenium Nanoparticles Inhibit Bacterial Growth While Promoting Mammalian Cell Growth.
Free full text in Europe PMC
Abstract
Background
Selenium is an essential trace element that is critical for many biological processes. Selenium nanoparticles (SeNPs) have shown more promise than other forms of selenium due to their low cytotoxicity and high bioavailability.Methods
In this work, a one-step method was demonstrated for fabricating bovine serum albumin (BSA) stabilized SeNPs using ascorbic acid as the reductant. Human dermal fibroblasts were used to assess mammalian cytotoxicity, and Staphylococcus aureus and Escherichia coli were used to assess antibacterial performance.Results
These SeNPs demonstrated increased fibroblast growth and reduced Staphylococcus aureus growth with a fibroblast IC50 value (>681 μg/mL) 1 order of magnitude higher than that for bacteria at day 1.Conclusion
This study demonstrated the promise of this synthesis process in achieving controllable selenium nanoparticle sizes without the use of strong basic solvents for improved antibacterial properties.Free full text
Green Synthesized BSA-Coated Selenium Nanoparticles Inhibit Bacterial Growth While Promoting Mammalian Cell Growth
Associated Data
Abstract
Background
Selenium is an essential trace element that is critical for many biological processes. Selenium nanoparticles (SeNPs) have shown more promise than other forms of selenium due to their low cytotoxicity and high bioavailability.
Methods
In this work, a one-step method was demonstrated for fabricating bovine serum albumin (BSA) stabilized SeNPs using ascorbic acid as the reductant. Human dermal fibroblasts were used to assess mammalian cytotoxicity, and Staphylococcus aureus and Escherichia coli were used to assess antibacterial performance.
Results
These SeNPs demonstrated increased fibroblast growth and reduced Staphylococcus aureus growth with a fibroblast IC50 value (>681 μg/mL) 1 order of magnitude higher than that for bacteria at day 1.
Conclusion
This study demonstrated the promise of this synthesis process in achieving controllable selenium nanoparticle sizes without the use of strong basic solvents for improved antibacterial properties.
Introduction
Selenium (Se) is an essential trace element vital for many important processes for mammalian cells. Selenium intake leads to the formation of selenoproteins, which are crucial in modulating oxidative stress levels and play critical roles in reproduction, thyroid hormone metabolism, DNA synthesis, and protection from oxidative damage and infection.1 Through the modulation of pro-/anti-oxidant activity, Se also modulates the immune system response and tunes macrophage responses as the immune system is particularly sensitive to the balance of oxidants and antioxidants.2 Selenium deficiency (<20 μg/day)3 may lead to Keshan’s disease,4 a cardiomyopathy disorder, and Kashin-Beck’s disease,5 a type of osteoarthritis. Recommended intake amounts for adults are between 55 and 400 μg/day.3
One promising area of research is the application of nanotechnology towards selenium fabrication and use.6–10 Nanoparticles (NPs) are particularly suitable as they possess high surface area to volume ratios, increased surface area, and increased interactions with biological targets, leading to higher availability and absorption by the host.11–13 In addition, selenium NPs (SeNPs) possess lower toxicity than their elemental form; in mice, the LD50 of selenomethionine was 25.6 mg Se/kg compared with 92.1 mg Se/kg for SeNPs.14 Researchers have shown that SeNPs may be used as a coating or directly in solution at dosages that reduce bacterial and cancerous growth while maintaining or promoting mammalian cell function.9,15–19
To fully utilize the potential of SeNPs, improved synthesis schemes are needed. Many SeNP schemes are multi-step processes that involve the use of harsh solvents, such as benzene and toluene,20 and/or strong bases, such as sodium hydroxide.21 Li and coworkers have found an alternative one-step method, using cysteine as a reductant.22 Instead of cysteine, Malhotra used ascorbic acid as a reductant for their system and dextran as a stabilizer.23 In this work, a synthesis scheme was developed using ascorbic acid and bovine serum albumin (BSA) as a stabilizer. Based on prior knowledge, SeNPs readily aggregate and are unstable without a stabilizer. BSA is a commonly used stabilizer that does not illicit toxic biological responses and is readily available. Here, these newly formed Se nanoparticles were then tested against mammalian and bacterial cell lines to assess their effect in modulating cellular activity.
Materials and Methods
Selenium Nanoparticle Synthesis
Bovine serum albumin (BSA, Sigma Aldrich, Saint Louis, MO)-coated selenium nanoparticles (SeNPs) were synthesized with sodium selenite, ascorbic acid and BSA in a one-step reaction. Specifically, 50 mM ascorbic acid (Sigma Aldrich) was added dropwise to 1 mL of an aqueous solution containing 100 mM sodium selenite and 10mg/mL BSA. Upon addition of the reductant into sodium selenite, the solution turned into light yellow and eventually into dark red. The reaction proceeded for 30 mins before the nanoparticles were collected by centrifugation (11,000 rpm at 15 min.) and were washed at least twice by dI H2O (dI H2O, Milli-Q system, EMD Millipore, Billerica, MA). The molar ratio of ascorbic acid to sodium selenite and agitation speed were altered at 2 levels (1:5 and 1:6 for 100 and 600 rpm, respectively) to generate the 4 reaction conditions (Table 1) as these conditions were found to produce SeNPs with biologically relevant sizes.
Table 1
Experimental Conditions Chosen for Cell Studies
| Molar Ratio (Sodium Selenite to Ascorbic Acid) | Agitation Speed (rpm) |
|---|---|
| 1:5 | 100 |
| 1:5 | 600 |
| 1:6 | 100 |
| 1:6 | 600 |
SeNP Characterization
The SeNPs were characterized by dynamic light scattering (DLS, 90Plus Zeta, Brookhaven Instruments, Holtsville, NY) with the manufacturer provided software to measure particle size. The NPs were first dried onto 300-mesh copper-coated carbon grids (Electron Microscopy Sciences, Hatfield, PA) before imaging by transmission electron microscopy (TEM, JEM-1010, Jeol, Peabody, MA). UV-visible spectra of the NPs were obtained from 200 to 1000 nm using a SpectraMax M3 (Molecular Devices, Sunnyvale, CA) to characterize the chemical properties of the SeNPs. The NPs were diluted 72x in dI H2O before measurements. Previous studies have further characterized SeNPs commonly used in our experiments.15–17
Mammalian Cell Activity Culture and Characterization
Human dermal fibroblasts (HDF) were used as the model cell line for cytotoxicity studies. Human dermal fibroblasts (HDF, Lonza, Basel, Switzerland) at passage numbers 5–10 were cultured in Dulbecco’s Modified Eagle Medium (DMEM, Sigma Aldrich) supplemented with 10% fetal bovine serum (FBS, Hyclone, Logan, UT) and 1% penicillin/streptomycin (P/S, Sigma Aldrich) in a humidified incubator at 37°C and a 5% CO2/95% air environment. HDFs were cultured to ~90% confluence, rinsed with Dulbecco’s phosphate-buffered saline (dPBS, Sigma Aldrich), and detached from the tissue culture surface with 0.25% trypsin-EDTA (Sigma-Aldrich).
HDF cells were then seeded into 96 well plates at 5000 cells/well, treated with 0.001–1 mg/mL selenium nanoparticles in 10x dilutions, and were grown for 1 day, 2 days and 4 days. Afterwards, cell activity was measured by the MTS (Cell Titer 96 Aqueous One Solution Cell Proliferation Assay, G3581 Promega) assay. The cell culture medium was aspirated before adding a 1:5 (media: MTS) solution for 2.5h and before measuring the absorbance of each well by a SpectraMaxM3 plate-reader at 490 nm. Controls included wells with no cells, and a standard curve was constructed with known cell numbers.
Bacteria Experiments
Escherichia coli (E. coli, ATCC no. 25922), multi-drug resistant (MDR) Escherichia coli (ATCC no. BAA-2471), and Staphylococcus aureus (S. aureus, ATCC no. 25923) were used as the model bacteria. For all bacteria tested, a single colony was picked from a stock agar plate and cultured overnight, 16–20 h, in a 3% tryptic soy broth (TSB, Sigma Aldrich) at 37 °C. Afterwards, the bacterial solution was diluted until the absorbance of the bacteria reached 0.52 at 562 nm for S. aureus and 1 at 600 nm for the E. coli species (both drug-resistant and non-drug resistant); these absorbances corresponded to a colony-forming unit count of 109 based on previous experiments.
The bacteria were then diluted to 106 CFU/mL for S. aureus and 105 for the E. coli species and were seeded at 100 μL/well in a 96-well plate. The bacteria were cultured with either no SeNPs (control) or 0.001–1-mg/mL SeNPs in 10x dilutions overnight (16–20 h.). For the next day, the bacterial solutions were diluted 105 fold and plated in 10-μL spots on an agar plate to determine the number of CFUs. The agar plate was cultured for another 12–16 h. before counting.
Statistics
All experiments were conducted in triplicate and repeated at least three times each. Analysis of variance (ANOVA) and Student’s t-tests were used to determine the significance in the changes in cellular activity.
Results
Selenium Nanoparticle Synthesis
SeNPs were formed by adding the reductant, 50 mM ascorbic acid, in specified molar ratios (Table 1) to an aqueous solution containing 100 mM sodium selenite and 10 mg/mL of BSA and were measured by DLS as a preliminary screen (Table 2). At a 1:2 molar ratio addition of sodium selenite to ascorbic acid, the particles generated were in the μm range while at a 1:4 ratio and above, the particles generated were in the nm range. Agitation showed different effects on the size of the nanoparticles, depending on the molar ratio. At a 1:2 ratio, agitation did not appreciably affect the size of the particles generated. At a 1:4 ratio, increases in agitation directly increased the size of the nanoparticles produced. Interestingly, at ratios of 1:5 and 1:6, intermediate agitation (400 rpm) reduced the nanoparticle size while high agitation (600 rpm) increased the nanoparticle size. Above a ratio of 1:4, the sizing of the nanoparticles at the same agitation was similar (including at a ratio of 1:8, data not shown), possibly suggesting that the reaction had plateaued and no further increases in reductant concentration would further affect the reaction. Similarly, agitation above 600 rpm (1100 and 1500 rpm, data not shown) did not appreciably change the nanoparticle size.
Table 2
Dynamic Light Scattering (DLS) Measurements of Selenium Nanoparticles (SeNPs) at Different Reaction Conditions
| Agitation | ||||
|---|---|---|---|---|
| 100 rpm | 400 rpm | 600 rpm | ||
| Molar ratio | 1:2 | 753 nm | 803 nm | 721 nm |
| 1:4 | 26 nm | 34 nm | 37 nm | |
| 1:5 | 23 nm | 15 nm | 42 nm | |
| 1:6 | 20 nm | 21 nm | 47 nm | |
Note: Shaded conditions were chosen to further cell studies
Following this initial screen, the shaded conditions (1:5 ratio at 100 rpm, 1:5 ratio at 600 rpm, 1:6 ratio at 100 rpm, and 1:6 ratio at 600 rpm) were chosen for further characterization and cellular testing due to their low polydispersity (Figure 1) and biological relevant sizing. Nanoparticles with dimensions between 10 and 100 nm in diameter are most effectively uptaken by the mammalian cells.13 The particles were imaged by TEM in order to confirm their sizing and geometry (Figure 2). As expected, the reaction generated the characteristic spherical nanoparticles, and ImageJ analysis of the TEM images showed that the nanoparticle distribution matched that from DLS (Figure 3).
Histogram generated from dynamic light scattering (DLS) in number mode for the following conditions: (A) 1:5 molar ratio of sodium selenite to ascorbic acid at 100 revolutions per minute (rpm); (B) 1:5 ratio at 600 rpm; (C) 1:6 ratio at 100 rpm; and (D) 1:6 ratio at 600 rpm.
Transmission electron microscopy (T.E.M.) images of selenium nanoparticles (SeNPs) for the following conditions: (A) 1:5 molar ratio sodium selenite to ascorbic acid at 100 revolutions per minute (rpm); (B) 1:5 ratio at 600 rpm; (C) 1:6 ratio at 100 rpm; and (D) 1:6 ratio at 600 rpm.
Histogram generated from transmission electron microscopy (T.E.M.) images for the following conditions: (A) 1:5 molar ratio of sodium selenite to ascorbic acid at 100 revolutions per minute (rpm); (B) 1:5 ratio at 600 rpm; (C) 1:6 ratio at 100 rpm; and (D) 1:6 ratio at 600 rpm.
UV-visible spectra captured the potential chemical changes due to the different reaction conditions (Figure 4). The absorbance of water was subtracted from that of the samples as water possesses strong signals in the 200-nm region which may interfere with the signal from the SeNPs. All four conditions yielded similar trends in the UV-Vis spectra and a peak absorbance at 290 nm.
UV-Visible spectrum from 200 to 1000 nm for selenium nanoparticles (SeNPs) for the following conditions: 1:5 molar ratio of sodium selenite to ascorbic acid at 100 revolutions per minute (rpm); 1:5 ratio at 600 rpm; 1:6 ratio at 100 rpm; and 1:6 ratio at 600 rpm.
Impact on Mammalian and Bacterial Cells
To assess the cytotoxicity of the SeNPs, human dermal fibroblasts (HDF) were chosen as the model system. An MTS assay was used to measure the cellular metabolic activity after exposure to SeNPs, and the signal of the treated cells was normalized to that of the no-treatment control (Figure 5). At the highest concentrations tested (1 and 0.1 mg/mL), the SeNPs showed substantial cytotoxicity to the HDFs. However, at 0.01 and 0.001 mg/mL, SeNPs increased the 1-day MTS signal of the HDF cells compared to the control (p < 0.01). ANOVA analysis showed that the HDF response to the 4-reaction conditions was not statistically different except at the 0.001-mg/mL concentration at the 1-day time point, where both 600-rpm reaction conditions showed improved MTS activity (21% and 13% increase for the 1:5 and 1:6 ratios, respectively). Both 1:5 ratio reaction conditions showed an increased MTS signal at 0.01 mg/mL (12% and 11% for 100 and 600 rpm, respectively). At 2 days, the difference was no longer statistically significant, and by 4 days, the SeNP treated cells showed reduced MTS activity (p < 0.001).
MTS signal for human dermal fibroblast (HDF) for selenium nanoparticle (SeNP) treated cells compared to no treatment at 1, 2, and 4 days. All tests were conducted in triplicate, N = 3. Data are average ± standard deviation. * p < 0.01, ** p < 0.001 compared to no-treatment control at the same day. NS = not statistically significant.
Next, the ability of SeNP treatment for resisting bacterial growth was tested against both gram-positive (S. aureus) and gram-negative bacteria (E. coli and MDR E. coli, Figure 6). At the 1-mg/mL concentration, SeNP achieved a 10-fold reduction in S. aureus growth at all conditions except at the 1:5 ratio and 100 rpm in a statistically significant manner (p < 0.01). At the next highest dose, S. aureus reduction was still statistically significant at the 1:6 ratio condition (p < 0.01), and the antibacterial performance was comparable to the 1-mg/mL dose (45% reduction at 0.1 mg/mL compared to 62% at 1 mg/mL for the 1:5 ratio at 100 rpm, 56% compared to 86% for the 1:5 ratio at 600 rpm, 74% compared to 91% for the 1:6 ratio at 100 rpm, and 72% compared to 87% for the 1:6 ratio at 600 rpm). The lower dosages did not show a statistically significant reduction compared to the control. Treatment against the gram-negative bacteria showed no significant difference with the control.
Colony-forming unit (CFU) of (A) Staphylococcus aureus, (B) multi-drug resistant (MDR) Escherichia coli, and (C) Escherichia coli after 1-day treatment with selenium nanoparticles (SeNP). All tests were conducted in triplicate, N = 3. Data are the average ± standard deviation. * p < 0.01 compared to no-treatment control. NS = not statistically significant.
Discussion
In this study, a novel synthesis scheme was proposed to fabricate SeNPs in a controllable and facile fashion that avoided the use of harsh solvents or bases. The parameters found to most influence nanoparticle size were agitation and molar ratio of reductant to reactant. The oxidation number is +4 for sodium selenite and 0 for elemental selenium. As such, four reduction reactions are required to transform the sodium selenite into SeNPs. Ascorbic acid has a reducing capacity of 1–2 so the 1:2 molar ratio is not enough to fully reduce selenite into elemental selenium, causing substantial aggregation. This is consistent with findings reported by Li and co-workers22 although the degree of aggregation is much more substantial in the current study.
At the 1:4 molar ratio, there is enough reductant to fully convert the selenite into SeNPs, yielding drastically different behavior. However, the molar ratio of the reductant is likely not in excess and would be more sensitive to changes in agitation. At the 1:5 and 1:6 ratios, the nanoparticle formation at the different agitations was very similar. It is likely that at these molar ratios, the reductant concentration reached an excess and further increases in reductant concentration would not affect the reaction.
The effect of agitation on the SeNP formation is similar to the mechanism first proposed by Li and Kaner.24 In their study, they found that mild/low agitation, 0–380 rpm, did not change the polyaniline particle diameter or distribution while high agitation, 1100 rpm, increased the size. Their proposed model suggested that nanoparticles formed initially by homogenous nucleation until the particles reached a critical size. At this point, Brownian motion and/or agitation will cause collisions between the different nanoparticle seeds, creating larger nanoparticles under a heterogeneous nucleation mechanism. In the absence of agitation, this heterogeneous nucleation becomes limited and the nanoparticle size remains small. This model is also true for other inorganic nanoparticles, such as silica colloids. Sarin et al25 observed a similar phenomenon where the nucleation of SeNP in the presence of a carbon substrate occurred as competition between homogeneous and heterogeneous nucleation, and other instances are highlighted here.26–28
The UV-visible spectra showed similar peaks for all four reaction conditions, suggesting that changes in the reaction conditions did not alter the chemical composition or shape of the nanoparticles. In Li’s study, changes in the molar ratio of the reductant to selenite directly affected the morphology of the Se nanostructure, which directly altered the UV-visible spectra.22 The UV-visible spectra (Figure 4) matched those reported by others for spherical SeNPs.22,29 TEM images (Figure 2) confirmed the formation of spherical SeNPs, and the distribution shown from the images matched those from the DLS measurements (Figures 1 and and33).
HDF were chosen as the model cell line as they have been widely used for testing cytotoxicity.7,30 The half-maximal inhibitory concentration (IC50) was determined for the reaction conditions at the different dosages of SeNP (Table 3). For the 1-day time point, HDF viability remained at or above 50% for all concentrations tested, ranging from 42% at the 1:6 ratio and 100 rpm condition to 50% at the 1:5 ratio conditions. The 2-day and 4-day IC50 values remained similar for the different reaction conditions. The IC50 values of these SeNPs were comparable to those fabricated from the more established method of using glutathione as a reductant and precipitating by bringing the pH into the alkaline region. Hassan reported an IC50 value of 59.61 μg/mL for HDFs grown after 3 days of incubation with SeNPs which was similar to the IC50 values reported here from the 2- and 4-day time points.
Table 3
IC50 Values of the Selenium Nanoparticles (SeNPs) on Human Dermal Fibroblasts (HDF) and Staphylococcus aureus (SA)
| Day 1 HDF-IC50 (µg/mL) | Day 2 HDF-IC50 (µg/mL) | Day 4 HDF-IC50 (µg/mL) | Day 1 SA-IC50 (µg/mL) | |
|---|---|---|---|---|
| 1:5100 | N/A | 59.24 | 9.30 | 334.27 |
| 1:5600 | N/A | 61.02 | 9.75 | 88.99 |
| 1:6100 | 681.85 | 66.42 | 7.41 | 49.24 |
| 1:6600 | 789.66 | 64.79 | 6.65 | 70.32 |
S. aureus and E. coli were chosen as the bacterial cell lines, because they are common bacterial contagions that are rapidly developing drug resistance.31 In addition, SeNP treatment towards these bacteria is well-characterized and serves as a good benchmark for evaluating the performance for this synthesis scheme. Overall, the bacterial performance matched previously reported performance.17,29 Here, SeNPs achieved a 10-fold reduction for S. aureus and IC50 values much lower than those for HDF treated at the same time (334 μg/mL for the 1:5 ratio at 100 rpm, 88.99 for the 1:5 ratio at 600 rpm, 49 for the 1:6 ratio at 100 rpm, and 70 for the 1:6 ratio at 600 rpm for S. aureus). In addition, the IC50 for HDF was an order of magnitude higher than the IC50 for S. aureus (Table 3) for all conditions tested except for the 1:5 ratio at 100-rpm reaction condition, giving a favorable safety window of at least 10:1 (at the 1:6 ratio at 600 rpm, IC50 HDF = 789 μg/mL/IC50 S. aureus = 70 μg/mL). Conversely, SeNPs were ineffective against both E. coli species. Reports in the literature have contrary effects of SeNP on E. coli; some researchers found antibacterial efficacy6,32,33 while others did not.29,34,35 At this moment, there is no conclusive mechanism for the bactericidal activity of SeNPs.
Generally, the modes of action for metallic particle-induced bacterial inhibition are through inactivation of vital proteins, generation of reactive oxygen species (ROS), membrane disruption, nutrient uptake interference, or genotoxicity.36 However, none of these proposed pathways fully accounted for reported anti-bacterial activity. Liu et al found that SeNP loaded into an anodized titanium nanotube repelled E. coli growth and identified three modes of action: membrane disruption, damage to adhesion-mediating proteins, and reactive oxygen species (ROS) generation.6 However, Zonaro found that the amount of ROS generated by SeNPs (221.1–345.2 nm) did not correlate with the bacterial inhibition.32 In addition, prior studies with SeNP-treated Staphylococcus epidermidis, a Gram-positive bacterium (submitted work) did not show damaged bacterial membranes, suggesting membrane disruption was not the primary mode of antibacterial activity and may account for why the SeNPs were ineffective against E. coli in this study. In general, some of the reported differences in bacterial response may be attributed to the different strains of bacteria used, and studies focusing on omics-based differences may better elucidate the mechanism of action and why there are contradictory reports in the literature.
In summary, a novel method for synthesizing BSA-coated SeNPs was reported here. The fabrication method was robust, facile, easily scalable, and controllable and avoided the use of harsh solvents or bases. Optimal agitation and reactant molar ratios were identified for generating SeNPs with biologically relevant dimensions. Similar to previous synthesis schemes,24,25 this method likely was initiated through homogeneous nucleation before proceeding into a heterogeneous nucleation phase. The nanoparticles here possessed comparable chemical properties as those from previous synthesis schemes towards HDF and bacterial cell culture. Future studies requiring the use of SeNPs may utilize this facile green reaction scheme for generating controllable and homogeneous effective SeNP populations.
Acknowledgments
The authors would like to thank the Department of Chemical Engineering at Northeastern University for funding, William Fowle for his help with the TEM, and the members of the Webster Nanomedicine Group for their invaluable assistance and help. R.H.Z.’s travel expenses were supported by Nankai University and lab expenses were supported by Northeastern University.
Disclosure
The authors report no conflicts of interest in this work.
References
Articles from International Journal of Nanomedicine are provided here courtesy of Dove Press
Full text links
Read article at publisher's site: https://doi.org/10.2147/ijn.s193886
Read article for free, from open access legal sources, via Unpaywall:
https://www.dovepress.com/getfile.php?fileID=55205
Citations & impact
Impact metrics
Citations of article over time
Article citations
Recent advances in the therapeutic applications of selenium nanoparticles.
Mol Biol Rep, 51(1):688, 25 May 2024
Cited by: 2 articles | PMID: 38796570 | PMCID: PMC11127871
Review
Free full text in Europe PMCSelenium Nanoparticle Activity against S. mutans Biofilms as a Potential Treatment Alternative for Periodontitis.
Pharmaceutics, 16(4):450, 25 Mar 2024
Cited by: 0 articles | PMID: 38675111 | PMCID: PMC11055075
Antimicrobial Activity of Selenium Nanoparticles (SeNPs) against Potentially Pathogenic Oral Microorganisms: A Scoping Review.
Pharmaceutics, 15(9):2253, 31 Aug 2023
Cited by: 2 articles | PMID: 37765222 | PMCID: PMC10537110
Review
Free full text in Europe PMCEvaluation of Antibacterial Activity of Selenium Nanoparticles against Food-Borne Pathogens.
Microorganisms, 11(6):1519, 07 Jun 2023
Cited by: 9 articles | PMID: 37375021 | PMCID: PMC10300849
Selenium-Fortified Kombucha-Pollen Beverage by In Situ Biosynthesized Selenium Nanoparticles with High Biocompatibility and Antioxidant Activity.
Antioxidants (Basel), 12(9):1711, 02 Sep 2023
Cited by: 4 articles | PMID: 37760014 | PMCID: PMC10525527
Go to all (20) article citations
Similar Articles
To arrive at the top five similar articles we use a word-weighted algorithm to compare words from the Title and Abstract of each citation.
Synthesis and characterization of biogenic selenium nanoparticles with antimicrobial properties made by Staphylococcus aureus, methicillin-resistant Staphylococcus aureus (MRSA), Escherichia coli, and Pseudomonas aeruginosa.
J Biomed Mater Res A, 106(5):1400-1412, 06 Feb 2018
Cited by: 35 articles | PMID: 29356322
In vitro evaluation of bone cements impregnated with selenium nanoparticles stabilized by phosphatidylcholine (PC) for application in bone.
J Biomater Appl, 35(3):385-404, 20 Jun 2020
Cited by: 4 articles | PMID: 32567484
Synthesis and Characterization of Selenium Nanoparticles-Lysozyme Nanohybrid System with Synergistic Antibacterial Properties.
Sci Rep, 10(1):510, 16 Jan 2020
Cited by: 48 articles | PMID: 31949299 | PMCID: PMC6965607
Advances in the Synthesis and Bioactivity of Polysaccharide Selenium Nanoparticles: A Review.
Mini Rev Med Chem, 24(16):1535-1554, 01 Jan 2024
Cited by: 0 articles | PMID: 38425115
Review