http://rdf.ncbi.nlm.nih.gov/pubchem/patent/CN-106282852-B
Outgoing Links
| Predicate | Object |
|---|---|
| classificationCPCAdditional | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B22F2998-10 |
| classificationCPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C22C47-04 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/C22C47-14 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B22F1-17 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B22F3-1035 http://rdf.ncbi.nlm.nih.gov/pubchem/patentcpc/B22F3-002 |
| classificationIPCInventive | http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C47-14 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/C22C47-04 http://rdf.ncbi.nlm.nih.gov/pubchem/patentipc/B22F3-10 |
| filingDate | 2016-09-18^^<http://www.w3.org/2001/XMLSchema#date> |
| grantDate | 2017-10-20^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationDate | 2017-10-20^^<http://www.w3.org/2001/XMLSchema#date> |
| publicationNumber | CN-106282852-B |
| titleOfInvention | A kind of low-temp liquid-phase sintering manufacturing process of hybrid metal fiber sintering felt serving |
| abstract | A kind of low-temp liquid-phase sintering manufacturing process of hybrid metal fiber sintering felt serving, is related to composite metal fiber.1) metallic fiber is cut into multistage on request, various metals segment of fiber is obtained；2) zinc and tin heating and melting are mixed into obtain metallic solution, then metallic fiber section is put into metallic solution, cooled down after pulling out；3) repeat step 2) until metallic fiber section surface all one layer of zinc-tin mixed layers of plating, obtain hybrid metal fiber, then be placed in grinding tool；4) hybrid metal fiber is compressed in the die cavity of grinding tool using grinding tool pressboard, hybrid metal fiber is full of whole die cavity；5) grinding tool is put into sintering furnace, makes hybrid metal fiber melting, N is passed through when sintering furnace temperature and being less than 100 DEG C 2 , H is passed through when sintering furnace temperature and reaching 200 DEG C 2 , zinc-tin metal is in the liquid state to hybrid metal fiber intersection points diffusion aggregation, after the temperature setting program of stove to be sintered is finished, and furnace cooling obtains hybrid metal fiber sintering felt serving. |