| abstract |
A crosslinked resin composition obtained by crosslinking a composition comprising (A) 95-10 wt. % of a propylene polymer and (B) 5-90 wt. % of an ethylene/ alpha -olefin copolymer having the following properties (I) to (iv) and prepared by copolymerizing ethylene with an alpha -olefin having 3 to 12 carbon atoms in the presence of a catalyst, said catalyst comprising a solid component and an organoaluminum compound, said solid component containing at least magnesium and titanium: -(i) Melt index 0.01-100 g/10 min -(ii) Density 0.860-0.910 g/cm3 -(iii) Maximum peak temperature not lower than 100 DEG C. - measured according to a - differential scanning - calorimetry (DSC) -(iv) Insolubles in boiling not less than 10 wt. % - n-hexane - |